摘要本文以天然多聚糖羧甲基壳聚糖和羧甲基纤维素为基体材料，通过氧化后的羧甲基纤维素与羧甲基壳聚糖发生的原位交联反应制备一种新型水凝胶敷料。结合药物传递技术，通过负载到水凝胶内的盐酸四环素的缓慢释放，获得具有良好抗菌性能的医用敷料。在体外系统评价了该载药水凝胶敷料的微观形貌、力学性能、溶胀性能、降解性能和抑菌性能。研究结果表明，该敷料具有良好的力学性能和生物降解性能，并且吸水性强，其吸水量可达自身重量的50倍。特别地，该载药水凝胶敷料释药时间可达48h以上，抑菌效果良好，有望能为伤口愈合提供长效有利的环境。87811

毕业论文关键词  水凝胶   多聚糖   敷料   抗菌性

毕业设计说明书外文摘要

Title   Antibacterial properties of medical polysaccharide dressings                                           

Abstract In this paper, we used natural polysaccharide carboxymethyl chitosan (CMCS) and carboxymethyl cellulose (CMC) as based materials。 By in-situ crosslinking reaction of oxidized carboxymethyl cellulose (OCMC) and carboxymethyl chitosan (CMCS), a novel hydrogel wound dressing is prepared。 Binding drug delivery technology, through the slow release of tetracycline hydrochloride (TH) which is loaded to the hydrogel, the medical dressing obtains excellent antibacterial properties。 Microstructure，mechanical properties, swelling behavior, degradation and antimicrobial properties of the drug-loaded hydrogel dressing have been systemly evaluated in vitro。 The results show that the dressing has good mechanical properties and biodegradability, and has an excellent water absorption of 50 times of its own weight。 In particular, the drug-loaded hydrogel dressing has the release time of up to 48h, and good antibacterial effect。 It is expected to be able to provide a favorable wound healing environment for a long term。

Keywords  hydrogel   Polysaccharide  wound dressing   antibacterial properties

目  次

1  引言 1

1。1  皮肤伤口形成及其愈合过程 1

1。2  医用敷料 2源-于,优Y尔E论W文.网wwW.yOueRw.com 原文+QQ752018`766

1。3  水凝胶敷料 3

1。4  壳聚糖和纤维素在敷料中的应用 4

1。5  敷料的抗菌性 6

1。6  课题的提出 8

2  实验 9

2。1  实验原料和仪器 9

2。2  羧甲基纤维素的氧化 9

2。3  水凝胶的制备 10

2。4  红外图谱分析 10

2。5  力学性能测试 11

2。6  溶胀性能测试 11

2。7  降解性能测试 11

2。8  红外图谱分析 11

2。9  负载盐酸四环素（TH）的水凝胶及其缓释性能测试 12

2。10  敷料抑菌性测试 12

3  结果与讨论 13

3。1  羧甲基纤维素的氧化