摘要铍青铜材料是典型的热处理强化合金材料，热处理工艺是合金取得优异性能的关键。通常我们用的是固溶处理和时效的热处理方法，本文主要对时效进行研究。在时效过程中必须对时间和温度严格控制，通过正交实验求出最佳时效工艺，最后通过XRD分析和金相显微组织观察探究其性能变化根本。87886

实验结果表明：时效过程有欠时效、正常时效和过时效三个阶段；铍青铜经320℃X2h时效后抗拉强度达到最大值1278MPa；340℃X2h时效处理后硬度达到最大值455。5HV；导电性能随着是时效过程的进行一直上升；时效过程铍青铜合金中有第二相的沉淀析出、长大和聚集。

毕业论文关键词  铍青铜  时效处理  强度   导电性 

毕业设计说明书外文摘要

Title  Optimization of heat treatment process and Study on  organization and properties of Beryllium bronze                 

AbstractBeryllium bronze is a typical heat treatment strengthened alloy material, and heat treatment process is the key to obtain excellent properties of the alloy。 We usually use the solution treatment and aging to strength Beryllium bronze,and we mainly studies the aging process in this paper。 In the aging process time and temperature must be strict control , through the orthogonal experiment to find the best aging process, finally, through the XRD analysis and organization observation to explore the fundamental changes in its performance。

The results show that the aging process is pided into less aging, normal aging and over aging; After 320℃ X 2h aging， tensile strength reached the maximum value 1278MPa; After 340℃ X 2h aging treatment, hardness reached maximum 455。5HV; Conductivity is a straight up with the aging process; and the precipitation of the second phase , grew up and aggregation in the aging process of QBe2 alloy。

Keywords  Beryllium bronze2 alloy   aging treatment  strength  conductivity

目   次

1  绪论 1

1。1  引言 1

1。2  铍青铜合金研究进展及应用领域 2

1。3  合金元素及杂质元素对铍青铜组织、性能的影响 3

1。4  铍青铜的热处理 5

1。4。1  固溶处理及其强化机理 5

1。4。2  时效处理及其强化方式 5

1。5  课题研究背景、意义及主要内容 6

1。5。1  背景及意义 6

1。5。2  主要研究内容 7

2  实验内容和方法 8

2。1  铍青铜合金材料的成分 8

2。2  实验所用器材及用途 8

2。3  实验内容 8

2。4  铍青铜合金力学性能测试 9

2。4。1  抗拉强度测试 9

2。4。2  显微硬度测试 9

2。5  导电性能测试 10

2。6  材料的组织形貌和相分析 11

3  时效处理对铍青铜组织和性能的研究 12

3。1  时效处理过程中微观组织变化