高强铝双轴肩搅拌摩擦头设计和工艺研究
高强铝是一种具有各种优良性能的材料，近年来在各个领域得到了广泛应用。同时，高强铝的焊接也存在着诸多难题，如焊接变形、软化、裂纹、气孔等。搅拌摩擦焊最大程度上缓解了因热输入导致的接头软化问题，因此特别适用于高强铝的焊接。
本次实验在之前实验的基础上选择了600转速和20焊速。在实验中，遇到了板材厚度过大，坡口不合适，螺纹未选好，摩擦头材料耐热性能不够等诸多问题，导致结果并不尽如人意。这些都是需要改善的。
关键词 搅拌摩擦焊 双轴肩 高强铝
毕业论文设计说明书外文摘要
Title Dual axle shoulder friction stir welding to aluminum
Abstract
Friction stir welding is a friction heat generated by the friction of the probe at the joint,material strongly plastic deformation,and the welding process of the welding seam is formed after the probe is deposited.The welding process has a simple economy, widely applicable, safety, no pollution, and many other advantages. Commonly used in friction stir welding is a single shaft shoulder more, probe into the seam but not through the seams. In contrast, bi-axial friction stir head with double shaft shoulder up and down to the shoulders, probe through the work-piece, which solved the problem of the uni-axial humeral back reserve quantity, also achieved better fixed effect of artifacts. Based on these considerations, formed the shoulder and bi-axial friction stir welding to welding of high strength aluminum work-piece process.× High strength aluminum is a kind of has a variety of excellent properties of material, in recent years has been widely applied in all fields. At the same time, the welding of high strength aluminum also exists many problems, such as welding deformation, softening, cracks, porosity, etc. Largest extent of friction stir welding joint softening problem caused by heat input, so especially suitable for the welding of high strength aluminum.× This experiment on the basis of the experiment before chose 600 rotation speed and welding speed. Encountered in the experiments, the thickness of the plate is too big, groove is not appropriate, thread did not choose good, the friction head material heat-resisting performance is not enough, and many other problems, lead to the result is not satisfactory. These are all need to improve.
Keywords Friction stir welding Dual axle shoulder aluminum
目 次
1 引言（或绪论） 1
1.1 搅拌摩擦焊 1
1.1.1 搅拌摩擦焊主要特点 2
1.1.2 搅拌摩擦焊应用领域 2
1.1.3 搅拌摩擦焊接的主要材料 2
上一篇：锂电池正极材料NCA的制备及研究
下一篇：铝镁异种合金搅拌摩擦焊