摘要：本论文以溶剂热法制备了Ni- MOF电极材料以及在反应釜中进行Ni-MOF和GO的复合构筑，通过扫描电镜和红外仪器进行形貌和成分的分析，并用三电极法，以循环伏安法，表征恒电流充放电循环寿命和电化学性质。结果表明：实验中含5mlGO合成的Ni基MOF的电化学性能最优，0.5A·g-1下的比电容值达到了927F·g-1，而Ni-MOF，在0.5A·g-1下比电容值却只有571Fg-1，说明Ni-MOF与GO达到了预期的复合目的，比不含GO的Ni-MOF样品的比电容高出许多。

毕业论文关键词：氧化石墨烯；储能；MOF；超级电容器；电化学性能

Study on the structure and electrochemical properties of ordered layered Ni-MOF/rGO Composites

Abstract： In this paper, solvent hot prepared Ni-based MOF electrode material as well as Ni-MOF and GO compound in a reaction vessel constructed and analyzed morphology and composition by scanning electron microscopy and infrared instruments, and three-electrode method for the recycling of volts Anfa, characterization constant current charge-discharge cycle life and electrochemical properties. The results showed that: experiments 5mlGO containing Ni-based MOF synthesis of optimal electrochemical performance than the capacitance value 0.5A·g-1 reached under 927F·g-1, The Ni-based MOF, in 0.5A·g-1 lower than the capacitance value but only 571F·g-1, described Ni-MOF and GO achieve the desired purpose complex, higher than the Ni-MOF-free GO sample a number of specific capacitance.

Keywords: Graphene oxide; Storage; MOF; Supercapacitor; Electrochemical performance

目  录

1 绪论 1

 1.1 超级电容器的研究进展 1

  1.1.1 超级电容器的简介 1

  1.1.2 超级电容器的分类 2

  1.1.3 超级电容器电极材料 3

 1.2 MOF结构与石墨烯的介绍及其应用 4

  1.2.1 MOF的简介 4

  1.2.2 MOF结构的介绍 4

 1.3 MOF修饰石墨烯复合超级电容器材料 5

  1.3.1 石墨烯的简介 5

  1.3.2 石墨烯制备方法 5

  1.3.3 石墨烯的应用 6

 1.4 选题的思路 7

2 实验部分 9

 2.1 实验原料及仪器 9

 2.2实验过程 10

  2.2.1 Ni-MOF前驱体的制备 10

  2.2.2 氧化石墨烯的制备 11

  2.2.3 Ni-MOF/rGO复合材料的制备 12

  2.2.4 电极的预处理 13

  2.2.5 工作电极的制备 14

 2.3测试方法： 14

  2.3.1 X射线衍射测试 14

  2.3.2 SEM电镜观察 15

  2.3.3 FT-IR测试 15

  2.3.4 TG-DSC测试 15

  2.3.5 电化学性能测试（循环伏安法） 15

3 结果与讨论 16

 3.1 氧化石墨烯（GO）合成与表征