热塑性含氟聚氨酯弹性体的研制
Study on fluorinated thermoplastic polyurethane elastomer
Abstract: In this paper, using the polybutylene adipate glycol ester glycol (PBA) or polytetramethylene ether glycol (PTMEG) as basic material and fluorinated polyether polyol (PF) and toluene diisocyanate (TDI) or two methylene diphenyl diisocyanate (MDI) reaction,By the addition of chain extender (BDO) reaction to prepare thermoplastic fluorinated polyurethane elastomer.The performance change and the change of fluorine content of polyurethane elastomer.The results show that, PBA and PTMEG changes in the contact angle of water, hardness, tensile strength, elastic modulus and elongation at break of great change.Indicates that the method of changing polyester and polyether which is established in this paper is helpful to find the best of fluorinated polyurethane elastomer ratio, can obtain the fluorine polyurethane materials with excellent performance.
Keywords: thermoplasticity；fluorination；polyurethane；manufacture
目 录
1.绪论 1
1.1 聚氨酯弹性体简述 1
1.1.1 聚氨酯材料制备来源和发现 1
1.1.2 TPU的主要特性有： 2
1.1.3 聚氨酯的用途 3
1.2 FTPU简述 4
1.2.1 FTPU材料制备来源和发现 4
1.2.2 含氟聚氨酯的合成 4
1.2.3 含氟聚氨酯的性能 6
1.3现有问题 8
1.4选题依据 8
1.5本论文的研究目的和意义 8
1.6研究内容 8
2.实验部分 9
2.1 原料及试剂 9
2.2试验方法 9
2.2.1 热塑性含氟聚氨酯弹性体制备 9
2.2.2 改变硬段含量和R值来研究热塑性含氟聚氨酯弹性体 10
2.3 分析表征 10
2.3.1 接触角测量仪表征FTPU弹性体的表面性能 10
2.3.2 万能材料实验机分析复合材料的的力学性能 11
2.3.3橡胶硬度计测试复合材料的硬度 12
2.3.4 聚氨酯冲击弹性试验机测量材料的冲击弹性 13
2.3.5红外光谱仪表征产物结构 13
2.3.6 DMA测试复合材料的玻璃化转变温度 14
3 结果与讨论 15
3.1 聚酯型热塑性含氟聚氨酯弹性体性能 15
3.1.1 聚酯型热塑性含氟聚氨酯弹性体力学性能 15
3.1.2 热性能 17
3.1.3 表面性能 18
3.2聚醚型热塑性含氟聚氨酯弹性体性能 20
3.2.1聚醚型热塑性含氟聚氨酯弹性体力学性能 20
3.2.2 热性能 22
3.3聚酯型与聚醚型热塑性含氟聚氨酯弹性体的对比 23
3.2.1小结 23
4 结 论 24
4.1热塑性含氟聚氨酯技术研究 24
下一篇：铝合金用钎剂中粘结材料的研究