功能单体对水性丙烯酸酯树脂性能的影响研究
毕业论文关键词：水性叔丙树脂；水性酮肼交联丙烯酸酯树脂；水性N-羟甲基丙烯酰胺交联丙烯酸酯树脂；光泽度；耐水性
Effect of functional monomer on the properties of water-based acrylic resin
Abstract: In this paper，the synthesis of different formulations under the outstanding overall performance of waterborne acrylic resins，selection and examine three different waterborne acrylic resin system，Mainly preparation of aqueous tert-carbon resin，acrylic ketone crosslinked acrylic resin for hydrazine，aqueous N-methylol acrylamide cross-linked acrylic water-based resins，and determining the basic properties of the aqueous resin(including：solid content 、viscosity、pencil hardness、gloss、abrasion resistance、water resistance、heat resistance etc). By FT-IR ( infrared spectroscopy ) and DMA (Dynamic Mechanical Analysis) resin coating structure and thermodynamic characterization of conduct. Experiment acrylate functional monomer modified resin was better wear resistance and water resistance of aqueous hydrazine ketones and acrylate resins crosslinked aqueous N- methylol acrylamide crosslinked acrylic resin having，while also increasing the hardness and gloss water-based acrylic resin.
Keywords: Acrylic resin aqueous tertiary carbon；Water-based ketone hydrazine crosslinking acrylic resin；Aqueous N-methylol acrylamide cross-linked acrylic water-based resins；Gloss；Water resistance
目 录
1. 绪论 1
1.1 水性丙烯酸酯聚合物的应用 1
1.2 丙烯酸酯树脂的特点 1
1.3 水性叔丙体系的概述 2
1.4 水性酮肼交联体系的概述 3
1.5 水性N-羟甲基丙烯酰胺交联体系的概述 3
1.6 水性树脂在水性壁纸介质方面的应用与其特点 4
1.7 本实验研究目的与意义 5
2. 实验 6
2.1 原料的名称、规格和来源 6
2.2 主要实验仪器与设备 6
2.3 水性树脂的反应机理 6
2.3.1 水性叔丙体系反应机理 6
2.3.2 水性酮肼交联体系交联反应机理 7
2.3.3 水性N-羟甲基丙烯酰胺体系交联反应机理 8
2.4 水性树脂合成基本反应及设计的Tg 9
2.4.1 水性叔丙树脂合成基本反应 9
2.4.2 水性酮肼交联丙烯酸酯树脂合成基本反应 9
2.4.3 水性N-羟甲基丙酰胺交联丙烯酸酯合成基本反应 10
2.4.4 共聚物Tg的计算方法及各体系的Tg 12
2.5 水性树脂合成工艺 13
2.5.1 水性叔丙树脂合成制备工艺 13
2.5.2 水性酮肼交联丙烯酸酯树脂合成制备工艺 14