摘要聚酰亚胺是一种高性能的高分子材料，在航空、航天、纳米、液晶、激光等领域都有广泛的应用1-2。以均苯四甲酸二酐（PMDA）, ４,４′－双（３－氨基苯氧基）二苯砜（BAPS） ，4,4＇-二氨基二苯醚(ODA)，3,3＇,4,4＇-联苯四羧酸二酐(S-BPDA )为原料，并依次通过流涎成型和热亚胺化的方法制备得PAA凝胶膜和聚酰亚胺（PI）薄膜。并借助热重分析（TGA）、动态力学分析（DMA）、差示热量扫描（DSC）对PAA及PI进行了测试与表征。分析聚合单体组成对材料性能的影响。43875

Abstract：  Polyimide is a kind of high performance polymer materials,which is widely used in aviation，aerospace，nano crystal，laser，etc1-2. PAA gel films and polyimide(PI) films were prepared through casting molding and thermal imidization, which were synthesized by 1,2,4,5-Benzenetetracarboxylic anhydride (PMDA)，bis[4-(3-aminophenoxy)phenyl](BAPS)，4,4'-oxybisbenzenamine(ODA)，3,3',4,4'-Biphenyltetracarboxylic acid dianhydride（S-BPDA）．And the performance of PAA and PI film were characterized with  Thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA) and differential scanning calorimetry (DSC)．Discussed the influence of monomer composition on the mechanical properties and thermal properties of PI．

毕业论文关键字：单体； 摩尔比； 聚酰亚胺； 性能  

 Keyword:  Monomer；  mole ratio ； Polyimide； Performance

目   录

1前言： 1

1.1研究背景 1

1.2研究现状 1

1.3研究意义及主要内容 2

1.4聚酰亚胺的合成方法 2

1.4.1 溶液缩聚法 2

1.4.2熔融缩聚法 3

1.4.3 界面缩聚法 3

1.4.4 气相沉积法 3

1.5聚酰亚胺薄膜的加工方法 3

1.5.1流延 3

1.5.1沉积 3

1.5.2喷涂 3

1.5.3拉伸 4

2 实验 4

2.1 主要的原料与试剂 4

2.2 PAA溶液的制备 5

2.3 PI薄膜的制备 6

2.4 实验仪器 6

2.4.1　傅立叶红外光谱仪(FTIR) 6

2.4.2　热重分析仪(TGA) 7

2.4.3　差示扫描量热仪(DSC) 7

2.4.4  动态力学分析（DMA） 7

3结果与讨论 7

3.1 二胺组成比例对PI薄膜力学性能和热性能的影响 7

3.2 不同二酐单体对PI薄膜力学性能和热性能的影响 11

4 结论 11

参考文献 12

致    谢 13

1前言：

1.1研究背景

     聚酰亚胺( PI) 在高分子材料中占有突出地位，特别是功能性聚酰亚胺是一类非常有发展前景的材料。聚酰亚胺是一种高性能材料，热稳定性优异、电性能和力学性能良好，因此它用途非常广泛，在电气绝缘和微电子工业等领域3有广泛的应用。在其他方面，聚酰亚胺薄膜也发挥了非常重要的作用，如塑料制品，纤维，树脂，薄膜，泡沫塑料，涂料和粘合剂等。近年来不少新的功能性聚酰亚胺薄膜产品被开发出来,而且应用技术方面也有了新的进展。