摘要本论文采用溶剂热法制备Co3O4,通过改变反应条件,包括钴盐种类、表面活性剂种类、沉淀剂种类、溶剂种类和加热温度获得不同的产物,考察不同反应条件对Co3O4形貌和粒径的影响,用红外光谱(FT-IR)、X-射线衍射(XRD)、透射电子显微镜(TEM)等手段对产物的结构和形貌进行表征,并通过产物催化高氯酸铵热分解反应来研究其催化性能。实验结果表明,制备条件的改变对产物形貌的影响不大,但会影响粒径大小。粒径不同的 Co3O4对AP热分解的催化作用差别较大。63803

毕业论文关键词  Co3O4  溶剂热法  催化活性  高氯酸铵  

毕业设计说明书(论文)外文摘要

Title The preparation and catalytic properties of Co3O4                                                                              

Abstract Co3O4 powders were prepared by solvothermal method under different conditions. All the as-prepared samples were characterized by FT-IR, X-ray diffraction (XRD) and scanning electron microscopy (SEM). Some samples were mixed with AP to study their catalytic properties. The results show that the change of conditions above has a little impact on the morphology, but it will affect the particle size. It’s possible that the particle size of Co3O4 has big differences in catalytic activity. 

Keywords  Co3O4  Solvothermal  Catalytic activity  Ammonium perchlorate        

1 绪论 1

1.1 四氧化三钴的性质 1

1.2 四氧化三钴的制备 1

1.2.1 热分解法 2

1.2.2 溶胶一凝胶法 4

1.2.3 沉淀法 4

1.2.4 水热合成法 5

1.2.5 溶剂热合成法 6

1.3 四氧化三钴的粒度和形貌研究现状 6

1.4 高氯酸铵的热分解 7

1.4.1 AP的热分解过程 7

1.4.2 AP的热分解的催化机制 7

1.5 本论文的主要内容 8

2 四氧化三钴的制备与表征 9

2.1 试剂与仪器 9

2.1.1 主要试剂 9

2.1.2 主要仪器 9

2.2 四氧化三钴的制备 9

2.3 四氧化三钴的表征 11

2.4 结果讨论与分析 11

2.4.1 钴盐种类对产物物相的影响 11

2.4.2 加热温度对产物形貌的影响 12

2.4.3 溶剂种类对产物形貌的影响 13

2.4.4 沉淀剂种类对产物形貌的影响 14

2.4.5 表面活性剂种类对产物形貌的影响 16

2.4.6 产物的红外表征 18

2.5 本章小结 18

3 四氧化三钴的催化性能研究 19

3.1 四氧化三钴催化高氯酸铵热分解实验

上一篇:MEMS灵巧起爆器电热常开微开关设计和制作方法研究
下一篇:石墨烯铁氧化物多元复合材料制备及电化学性能

氧化石墨负载MOFs的制备及...

纳米二氧化钛的机械粉碎...

铌酸钾-铌酸钴钡氧化物陶瓷的性能研究

介孔二氧化硅载药微囊表面磁性修饰

钙钛矿型氧化物电催化剂的制备与性能研究

二氧化锡纳米微球制备和光催化

BiVO4光催化剂的改性及其催化氧化性能研究

大规模MIMO系统的发展研究现状

PCI+PID算法直流力矩电机速...

高效课堂教师问卷调查表

提高小學语文課堂朗读教...

浅析施工企业保理融资成...

遥感土地用变化监测国内外研究现状

MNL模型历史城区居民活动...

从企业eHR建设谈管理信息...

《水浒传》中血腥暴力研...

小型通用机器人控制系统设计任务书