摘要导电聚合物具有很大的电导率范围,还具有良好的光学性能、机械性能、可 加工性和电化学活性,其在二次电池、电致变色装置、电催化等领域拥有广阔的 应用前景。聚苯胺因其众多的优点已成为导电聚合物杰出的代表,也是目前受到 研究最多最具应用价值的材料。但它的活性却受到溶液 pH 的严重制约。为了提 高聚苯胺的 pH 适应范围,本实验应用循环伏安法在三电极(工作电极,辅助电 极,甘汞电极)系统下寻找天青 B 与苯胺共聚的最佳条件,制备聚天青 B/聚苯 胺复合膜并测定其在 pH 1~12 的硫酸钠溶液中的电化学活性。最终制成了在 pH 12 的条件下具有电化学活性的聚天青 B/聚苯胺复合膜。82620

毕业论文关键词:循环伏安法;电催化性能; 聚天青 B/聚苯胺双层膜

Abstract Conducting polymers have a wide range of conductivity, it also has good optical properties, mechanical properties, processability and electrochemical activity。 It has been widely applied in the fields of the secondary batteries, electrically induced discoloration devices, and electric catalysis。  Polyaniline  is  an  outstanding conductive polymer because of its advantages, and it is one of the most studied materials currently。 But its activity has been severely constrained by the solution pH。 In order to improve its pH dependence, polyaniline and poly(azure B) composie is prepared by using cyclic voltammetry in a three electrode system。 The resultant poly(azure B)/polyaniline composite film is measured in a 0。5 mol dm-3 Na2SO4 solution with pH 1-12。 Finally, the poly(azure B)/polyaniline composite film still has electrochemical activity at pH 12。

Keywords: cyclic voltammetry ; electrocatalytic properties ; Poly(azure B)/polyaniline bilayer;;

目录

第一章 绪论 1

1。1 导电聚合物简介 1

1。1。1 导电聚合物的发现 1

1。1。2 导电聚合物的概念 1

1。1。3 导电聚合物的特点 1

1。2 导电聚合物的合成及研究方法 2

1。2。1 导电聚合物的合成方法 2

1。2。2 导电聚合物的性能表征方法 3

1。3 导电聚合物的分类、导电机理及应用 4

1。3。1 复合型导电聚合物材料 4

1。3。2 结构型导电聚合物材料 5

1。4 导电聚合物的国内外研究状况 7

1。5 导电聚合物材料前景 8

第二章 实验部分 9

2。1 仪器与试剂 9

第三章 结果与讨论 10

3。1 聚苯胺的合成 10

3。2 聚天青 B 的合成

上一篇:蜡梅碱类似物的合成研究
下一篇:日处理3000吨皮革废水处理工程设计+CAD图纸

环保膨胀型钢结构防火涂料的制备与性能研究

食用香精中定香剂的筛选与设计

聚醚改性硅油的制备与性能研究

钙钛矿型氧化物电催化剂的制备与性能研究

遮光性白色聚酰亚胺薄膜的制备与性能

MOF支撑铁基电极材料的制备与储锂性能研究

丹徒区312国道旁菜地土壤...

小型通用机器人控制系统设计任务书

《水浒传》中血腥暴力研...

高效课堂教师问卷调查表

遥感土地用变化监测国内外研究现状

浅析施工企业保理融资成...

MNL模型历史城区居民活动...

提高小學语文課堂朗读教...

大规模MIMO系统的发展研究现状

PCI+PID算法直流力矩电机速...

从企业eHR建设谈管理信息...