摘要单组分化是环氧树脂应用中极具吸引力的一个发展方向，为使固化剂的使用更加方便并延长单组分化后环氧树脂体系在常温下的贮存时间，需进一步开发潜伏性固化剂。本文采用微胶囊技术，通过溶液蒸发法以PMMA和2PZ分别作为壁材、芯材制备了固化剂微胶囊，并表征了其形貌，组成等。通过示差扫描量热仪研究了加入微胶囊后环氧树脂体系的固化过程得微胶囊对固化过程有延迟作用，且固化反应过程复杂。43879

    Single group of differentiation is an attractive direction in the  application of epoxy resin. In order to make the use of the Curing agent is more convenient and prolong the storage time of epoxy resin system after single group of differentiation at room temperature.we need to further explore the field of Latent curing agent .In this essay ,I plan to make microcapsulated Curing agent using PMMA as wall material,2PZ as core material through microcapsule technology and  solution evaporation method . Then we characterize it to study its  morphology, composition etc. Through  the DSC determination of curing process of epoxy resin system , analysis showed that the microcapsules had a delayed action on the curing process, and the curing reaction process is complex.

毕业论文关键词：固化剂； 微胶囊； 潜伏性固化剂 

Keyword: Curing agent；  microcapsule； Latent curing agent ；

目   录

一 引言 4

二 实验部分 6

2.1 实验原料 6

2.2 实验仪器 6

2.3 PMMA微球的制备 7

2.4 不同芯材壁材质量比例的2PZ/PMMA微胶囊的制备 7

2.5 不同的乳化液浓度的2PZ/PMMA微胶囊的制备 7

三 微胶囊的测试及表征 8

3.1 形貌表征：扫描电镜（SEM） 8

3.2 化学结构表征：傅立叶变换红外光谱（FTIR） 8

3.3 成分分析：热重分析（TGA） 8

3.4 固化动力研究： 8

四 结果与讨论 9

4.1 PZ/PMMA微胶囊及PMMA微球的成分分析 9

4.2 2PZ/PMMA微胶囊组成含量分析 9

4.2.1 不同芯材壁材材料的质量比对2PZ含量的影响 10

4.2.2 不同乳化剂浓度对2PZ含量的影响 11

4.3 环氧树脂固化动力学分析 11

4.3.1 不同升温速率对固化的影响 12

4.3.2 不同芯壁材质量比制得的2PZ/PMMA微胶囊的固化 13