B7钢的淬透性影响研究+文献综述
毕业论文关键词：B7钢；马氏体；冷却介质；淬透性
Abstract
The thesis is about B7 steel samples of 6.5mm radius in quenching temperature 830~890℃, holding time 60~120min, using water as the cooling medium and the water temperature is at 10~90℃ range for the hardenability test research of different heat treatment conditions. The hardenability of B7 steel is mainly affected by the temperature of the cooling medium, and the higher the temperature of the cooling medium is, the more content non martensite quenching microstructure (troostite) of B7 steel will be，but the total content not more than 50%. When in quenching temperature 860 ℃, holding time 60 min, water temperature ≤60 ℃, this size of B7 steel samples can be complete quenched, the hardness is 47.4HRC, and the depth of hardened layer is about 6mm; when the water temperature exceeds 60 ℃, the non martensite microstructure content of B7 steel samples is more than 50%.
KeyWords：B7 steel；martensite；cooling medium；hardenability
目录
1 文献综述 3
1.1 课题研究的目的和意义 3
1.2 B7钢简介 3
1.2.1 B7钢的成分 3
1.2.2 B7钢的工艺 3
1.2.3 B7钢的性能 4
1.2.4 B7钢的应用 4
1.3 钢的淬火 4
1.3.1 淬火工艺参数的确定 4
1.4 淬透性概述 6
1.4.1 淬透性的概念 6
1.4.2 淬透性的机理 6
1.4.3 淬透性的影响因素 7
1.4.4 淬透性的测定方法 8
1.4.5 淬透性指标的应用 8
1.4.6 实现淬透性指标的影晌因素 8
1.5 正交试验法简述 9
1.5.1 指标 10
1.5.2 因素 10
1.5.3 位级 10
1.6 国内外相关研究 10
1.6.1 国外论文的研究 10
1.6.2 国内论文的研究 11
1.7 相近钢种42CrMo的研究 11
1.7.1 42CrMo简介 11
1.7.2 冷却条件对42CrMo的影响 11
2 实验部分 13
2.1 实验内容 13
2.2 实验原理 13
2.3 实验方法 13
2.3.1 主要方法 13
2.3.2 测定方法 13
2.3.3 分析方法 14
2.3 实验方案 15
2.3.1 方案设计 15
下一篇：改型高温合金的高温氧化行为的研究