合金元素对Al-Mn合金箔带强度的影响
然而由于厚度的减薄使得AL-MN合金的强度，抗蠕变，腐蚀等性能难以达标，因此对于AL-MN合金内微量合金元素的添加成为了对强度等性能控制的主要手段，然后对于合金元素种类以及数量的掌握又都是相对未知的，相对过多或者过少的量都可能导致元素之间电极电位的改变，不同的元素所带来性能上的提高也是各不相同，所以合金元素对于AL-MN合金强度的影响便是重点之一，对其的研究也是十分具有意义以及必要的。21264
毕业论文关键词：铝合金；高温强度；散热器
Abstract
As the car radiator with aluminum foil instead of the traditional copper foil, weight could be reduced 37-45%, United States authorities test results showed that the Vehicle weight could be reduced by 10%, fuel consumption could be reduced by 8%, emissions could be reduced by 28%, and AL-MN alloy foil thickness could only be used in cars to 0.08mm, so thinner to 0.06mm arising from resource savings were considerable.
However, due to thickness of reduction made strength AL-MN alloy,creep,corrosion and other performance standards is difficult, so for adding the AL-MN alloy micro alloying elements became the primary means of controlling the strength and other properties, then the alloy type and number of control elements were relatively unknown, too much or too little relative to the amount of change may cause a potential difference between the electrode elements, different elements of the performance improvement brought also different, So one of the alloying elements affect the strength of the alloy AL-MN is the focus of their research is very meaningful and necessary.
Key words: Aluminum alloy; High-temperature strength; Radiator
目 录
1文献综述 1
1.1国内外技术进展及展望 1
1.1.1复合铝箔的应用与技术进展 1
1.1.2 铝合金在汽车散热器中的优势 2
1.1.3铝合金散热器的技术要求及特点 2
1.1.4未来国内技术的发展 3
1.2复合铝箔的材料与性能 3
1.2.1复合铝箔材料结构 3
1.2.2复合铝箔的主要性能 4
1.3Al-Mn合金发展与存在问题 5
1.3.1Al-Mn合金发展方向 5
1.3.2 Al-Mn合金发展存在的技术问题 5
1.4Al-Mn合金的一些微量元素 6
1.4.1.主要合金元素的添加 6
1.4.2.微量元素的添加 6
2选题的目的及意义 7
3研究内容及意义 8
3.1研究内容 8
3.1.1实验条件 8
3.2 研究目的及目标 8
4实验方法 8
5实验详细过程 9
5.1配方的配制 9
5.1.1第十次实验 9
5.1.2 第十一次实验 9
5.1.3 第十二次实验 9
5.2 配方的称量 10
5.3熔炼浇筑及表面处理 10
5.4轧制 12
5.5抗下垂性实验 14
5.6显微硬度实验 19
5.7金相组织实验 20
6实验数据及结果 24
6.1显微硬度HV值 24
6.2 抗下垂实验下垂值 26
下一篇：稀土掺杂氧化钇的制备与性能研究