摘要近年来，由于超疏水表面在生产和生活中的重要应用而引起了科研工作者的广泛关注。人工制备超疏水表面的时间虽然不长，但其发展速度极快，有效的制备超疏水表面的方法也越来越多。然而，目前这些方法的粗糙构造仍然是通过单纯的人工模仿，各种不同的制备方法还存在着各种各样的缺点和局限性。本研究利用木材为模板，通过对木炭表面电镀铜等金属的方法，获得具有植物表面构造的超疏水金属表面。测试并研究这种材料的疏水性能，探索模板结构对材料疏水性能的促进作用，揭示分级构造对材料疏水性能的影响。87530

毕业论文关键词  超疏水  碳  Cu  接触角   

毕业设计说明书外文摘要

Title  Study on preparation and properties of wood structure  super hydrophobic metal surface                       

Abstract In recent years, due to the important application of super hydrophobic surface in production and life, it has attracted the attention of researchers。 Although the artificial preparation of super hydrophobic surface is not long, but its development speed is very fast, effective method for the preparation of super hydrophobic surface is also increasing 。However, the rough structure of these methods is still a simple artificial imitation, and a variety of shortcomings and limitations exist in a variety of different preparation methods。 In this study, we obtained the surface structure of super hydrophobic metal surface with the method of electroplating copper or other metals on the surface of charcoal。 Test and study the hydrophobic property of this material, explore the promoting effect of the template structure on the hydrophobic property of the material, reveal the effects of grading structure on the hydrophobic properties of materials。源-于Y优~尔^论:文.网www.chuibin.com 原文+QQ7520`18766

Keywords  Superhyphobic  Carbon  Cu  Contact angel (CA) 

目   次

1  绪论 1

1。1  引言 1

1。2  超疏水表面的性能 1

1。3  超疏水表面的理论基础 2

1。4  超疏水表面的应用 3

1。5  超疏水表面的制备 4

1。6  超疏水金属表面制备技术存在的问题及展望 5

1。7  选题的目的及研究意义 5

2  木材的疏水性极其表面性能研究 6

2。1  引言 6

2。2  实验部分 7

2。3  天然木材疏水性测试 9

2。4  木炭的疏水性极其表面性能分析 10

2。5  本章小结 13

3  超疏水金属表面的制备及其性能研究 14

3。1  引言 14

3。2  实验部分 14

3。3  电镀实验结果与讨论 15

3。4  本章小结 20

结  论 22

致  谢 23

参 考 文 献 24