利用固体废弃物制备硅酸钙保温材料
关键词 加气混凝土 水化硅酸钙 托贝莫来石 硅酸钙绝热材料
说明书（毕业论文）外文摘要
Title Prepare calcium silicate insulation materials by using solid waste
Abstract
In recent years,as people’s living standard continues to improve,the society increases it’s demands of housing.This phenomenon has brung a large number of construction,which creates the pollution of industrial litter and the waste of raw materials.On the other hand,energy shortages is becoming a major bottleneck of industrial production.This paper studies the use of aerated concrete waste and other industrial waste as well as pure CaO, using a static method of hydrothermal synthesis process for preparing calcium silicate insulation materials.With the help of different instruments,such as XRD,we analyzed the morphology of Tobermorite type calcium insulating materials,which are made bydifferent reaction conditions.Finally we tested the specific surface area ， pore size and thermal conductivity.
Keywords zirconium slag aerated waste diatomite tobermorite calcium insulating material
1 绪论 1
1.1 课题背景 1
1.2 硅酸钙绝热材料的研究及发展现状 1
1.3 托贝莫来石型硅酸钙绝热材料 2
1.4硬硅钙石型硅酸钙绝热材料 3
1.5硅酸钙绝热材料的制备 3
1.5.1 托贝莫来石型绝热材料的合成制备 3
1.5.2硬硅钙石型绝热材料的合成制备 5
1.6 加气混凝土 5
1.7 锆渣的性质及利用 5
1.7.1 锆渣的形成过程 6
1.7.2 锆渣利用的研究现状 6
1.7.3 锆渣利用的发展前景 7
1.8 几种硅酸钙绝热材料的简介 7
1.8.1 憎水型微孔硅酸钙绝热制品 7
1.8.2 超轻憎水硬硅钙石型硅酸钙绝热制品 7
1.8.3 纤文增强二氧化硅气凝胶绝热材料 7
1.9 水热合成法 8
1.9.1 水热合成法的原理 8
1.10 本课题研究的目的及意义 9
1.11 研究的重点及创新点 9
2 实验过程及检测方法 9
2.1 实验原料 10
2.1.1 硅质原料 10
2.1.2 钙质原料 10
2.2 实验设备 10
2.3 实验工艺及流程及测试方法 12
2.4 热膨胀率和导热系数的测定方法 13
2.4.1热膨胀率的测定 13
2.4.2 导热系数的测定 13
2.5 比表面积及孔径的测定 14
2.5.1比表面积测试原理 14
2.5.2 孔径分布测定原理 16