改性剂对水玻璃砂溃散强度影响研究
毕业论文关键词：有机酯；改性剂；CO2吹气硬化；水玻璃砂；溃散强度
Research on Effect of Modification agent of Water Glass Sand Collapsibility Strength
Abstract: The effect of modification agent and hardening process on properties of water glass sand was studied. The modified agents of Polyacrylamide and sodium dodecylsulphate were used. Single hardening processes which were used were dried hardening, blowing CO2 gas hardening. Compound hardening processes which was used was organic ester - blowing CO2 gas hardening. The experimental results showed that: the addition of water glass content is low, the residual strength is small ,collapsibility is better. Water glass add a certain amount of time, adding the modifier of water glass sand residual strength is lower than that of the non modified agent good collapsibility. Blowing CO2 and organic ester hardening and drying and hardening, blowing CO2 hardening, hardening effect is better good collapsibility. Blowing hardening, modifier polyacrylamide, adding 0.3~0.9 percent, blowing time more long residual strength the lower the better collapsibility; modifier is sodium dodecylsulphate, adding 0.3~0.9 percent, blowing time shorter residual strength is low collapsibility is better.
Key words: Organic ester; Modification agent; CO2 gas hardening; Water glass sand; Collapsibility Strength
目录
1.前言 1
1.1水玻璃简介 1
1.2水玻璃的发展 2
1.3水玻璃的改性 2
1.3.1.水玻璃的物理改性 3
1.3.2.水玻璃的化学改性 3
1.3.3.水玻璃的复合改性 4
1.4水玻璃砂溃散性能研究进展 5
1.4.1溃散剂 5
1.4.2水玻璃改性 6
1.4.3硬化工艺 6
1.5选题的目的和意义 7
1.6课题的研究内容和目标 8
1.6.1研究内容 8
1.6.2研究目标 8
2.实验 9
2.1试验材料 9
2.2 试验方案 9
2.2.1未改性水玻璃加入量对水玻璃砂溃散性能的影响 9
2.2.2改性剂加入量对水玻璃砂溃散强度的影响 9
2.2.3硬化工艺对水玻璃砂溃散强度的影响 10
2.2.4吹气时间对水玻璃砂溃散强度的影响 10
2.2.5改性剂加入量和吹气时间对水玻璃砂溃散强度的影响 11
2.2.6改性水玻璃加入量和吹气时间对水玻璃砂溃散强度的影响 11
2.3试验设备 12
2.3.1 SHN辗轮式混砂机 12
2.3.2 XQY-Ⅱ智能型砂强度机 13
2.3.3 SAH树脂砂制样机 13
2.3.4 SX-4-10箱式电阻炉 14
2.3.5 101-3型干燥箱 14
2.3.6 JB50-D搅拌器 15
上一篇：护手霜的流变性研究+文献综述
下一篇：电解铜箔表面电镀铜改性工艺研究