含乳酸添加剂的酸性化学镀镍-磷合金工艺研究
毕业论文关键词：正交实验；糖精；尿素；镀层厚度；沉积速度
Study on the process of acid chemical plating nickel phosphorus alloy containing lactic acid additives
Abstract: This topic through orthogonal experiment analysis seq hypophosphite as a reducing agent in the electroless plating solution containing lactic acid which were added saccharin and urea,and changing the amount of urea and saccharin and plating temperature change,under different temperatures,coating thickness,deposition rate,nickel-phosphorus content and change the relationship between the content of the bath additives.EDS analysis using a nickel- phosphorus content,to investigate the mechanism of saccharin,urea additive.By studying the experimental results showed that:at 30℃~70℃ base plating bath (nickel sulfate 27g/L,sodium hypophosphite 21g/L,lactic acid 20g/L,sodium acetate,20g/L,theorem 2mg/L,pH6.4)add different mass saccharin urea,coating thickness and deposition rate exists highest point,and the highest point of the thickness and deposition rate increases with the additive quality,constantly moving towards the direction of low temperature.
Keywords: orthogonal; urea; saccharin; coating thickness; deposition rate
目 录
1前言 1
1.1 课题研究的背景 1
1.2 目的和意义 1
1.3 乳酸添加剂下酸性化学镀镍-磷研究现状 2
1.4 乳酸添加剂下酸性镀镍-磷的特点 3
1.5 课题研究的内容 4
2 实验部分 5
2.1 乳酸添加剂下酸性化学镀镍-磷的原理 5
2.2 化学镀Ni-P溶液的配方 6
2.2.1 化学镀镍-磷溶液的的组成 6
2.2.2 化学镀镍-磷组成的作用 6
2.2.3 化学镀镍-磷组成的影响 7
2.2.4 化学镀中的有害成分 9
2.3 主要实验试剂和主要实验仪器设备 9
2.3.1 主要实验化学试剂 9
2.2.2 主要实验仪器和设备 9
2.4 化学镀实验步骤 10
2.4.1 镀液配制步骤 10
2.4.2 镀液分析与调整 10
2.4.3 化学镀工艺流程 10
2.5 化学方案设计 11
2.5.1 温度对化学镀Ni-P性能影响实验配方以及工艺设计 11
2.5.2 不同添加剂对化学镀Ni-P性能影响实验配方以及工艺设计 12
2.6 镀层性能测试 12
2.6.1 镀层厚度测试 12
2.6.2 镀层镍-磷含量测试 13
3 数据分析和讨论 14
3.1 实验数据及分析 14
3.1.1 不同温度下添加剂对化学镀镍-磷合金的影响 14
3.1.2 不同添加剂下添加剂对化学镀镍-磷合金的影响 16
3.1.3 SEM扫描电镜图片的测试 17
下一篇：磷酸铁锂合成技术与电化学性能