界面增容制备芳纶增强聚甲醛复合材料
毕业论文关键词： 聚甲醛；芳纶；EAA；复合材料；耐摩擦性能
Research of composite of aramid fiber reinforced by formaldehyde by EAA interfacial compatibility
Abstract：This paper mainly studies the modification of high wear resistance properties of the composite materials of formaldehyde.The effect of aramid fiber on the interfacial compatibility was modified by EAA coated aramid fiber.And the modified aramid fiber is the reinforcing material.The composites were prepared by the formaldehyde resin.The mechanical properties of the composites include tensile properties, impact, bending and wear resistance, and the cross section of the composites are studied.The results of the study:When the ratio of EAA to aramid fiber was 1:5 and the addition of aramid fiber was 3%,The friction resistance of the composite was the best,and the comprehensive performance was the best.
Keyword: Formaldehyde; Aramid fiber; EAA; composite; friction resistance
目 录
1 绪论 1
1.1 聚甲醛复合材料概述 1
1.1.1 聚甲醛的改性发展方向 1
1.1.2 芳纶表面改性技术的进展 3
1.2 甲醛复合材料的特点及性能 5
1.2.1 聚甲醛复合材料的特点 5
1.2.2 聚甲醛复合材料的性能 5
1.3 聚甲醛复合材料的应用领域 5
1.4 课题研究的目的和意义 6
1.4.1 研究目的 6
1.4.2 研究意义 6
1.5 课题研究内容 7
2 实验部分 8
2.1 实验用主要原料 8
2.2 实验用仪器设备 8
2.3 实验过程 9
2.3.1 实验流程图 9
2.3.2 复合材料实验配方的确定 10
2.3.3 聚甲醛复合材料中芳纶的处理 10
2.3.4 聚甲醛复合材料的制备 11
2.4 性能测试 11
2.4.1 拉伸性能测定 11
2.4.2 抗冲击性能测定 12
2.4.3 弯曲性能测定 12
2.4.4 耐摩性能测定 12
3 结果与讨论 13
3.1 芳纶纤文处理配方比例及添加量的不同对复合材料力学性能的影响 13
3.1.1 芳纶纤文处理配方比例及添加量的不同对材料冲击性能的影响 13
3.1.2 芳纶纤文处理配方比例及添加量的不同对材料拉伸性能的影响 14
3.1.3 芳纶纤文处理配方比例及添加量的不同对材料弯曲性能的影响 15
3.2 芳纶纤文添加比例及添加量的不同对复合材料力学性能的影响 17
4 结论 19
致谢 20
参考文献 21
1 绪论
1.1 聚甲醛复合材料概述
广义上，聚甲醛复合材料是以聚甲醛树脂为基体材料，表面改性纤文作为增强材料经一定的工艺复合而成的多相材料，且通过良好的界面结合作用使得各种材料在使用性能上相互取长补短，从而使得最终复合的材料的综合性能远远比原各组分材料的性能优越，且能满足各种不同的生产需求，继而从实际意义上达到“1+1＞2”的复合效果。其中，增强相材料多采用纤文如芳纶纤文，主要有分担载荷的作用。