高分子添加剂对氧化钛纳米管快速生长的影响
毕业论文关键词 TiO2纳米管 高分子添加剂 阳极氧化法 快速生长
Title Effect of Polymer Additives on the Rapid Growth of Titanium Oxide Nanotubes
Abstract TiO2 nanotubes have broad prospects due to their unique photophysical properties, but the growth rate of it is too slow to meet the requirement of practical applications. In this work, we prepared TiO2 nanotubes by anodic oxidation, and make them grow steadily and orderly through adding polyvinyl alcohol (PVA), polyethylene glycol (PEG), lactic acid (LA) and other additives in the electrolyte by controling additive concentration, anodic oxidation voltage or current density. Then, we used field-emission scanning electron microscope to analyse the morphological characterization of the length and diameter of the TiO2 nanotubes. Finally, the electrochemical properties of the TiO2 nanotubes were studied. The results shows that the addition of PVA and LA has an good impact on the balance current and voltage of anodic oxidation which can prevent the phenomenon of high field breakdown. The 57.67 m long TiO2 nanotubes can be prepared successfully by anodizing for 0.5 hour at a current density of 50 mA/cm-2 in a typical electrolyte containing 0.2 wt% PVA and it is arranged orderly with structure intactly. The areal specific capacitance is 48.710 mF/cm2 high. In conclusion, it is a feasible method for rapid preparation of TiO2 nanotubes to add polymer additives in electrolyte.
Keywords TiO2 nanotubes polymer additive anodic oxidation rapid growth
目次
1绪论.....1
1.1课题背景及研究意义..1
1.2TiO2纳米管的形成机理..1
1.3TiO2纳米管形态的影响因素..2
1.3.1电解液组成的影响..2
1.3.2氧化电压的影响4
1.3.3电解液温度的影响..4
1.4本文的主要研究目与研究内容....4
1.4.1研究目的4
1.4.2研究内容4
2TiO2纳米管的制备及添加剂对氧化过程的影响....5
2.1实验内容....5
2.1.1实验试剂与实验仪器....5
2.2实验过程....6
2.2.1实验样品的预处理..6
2.2.2电解液的配制....6
2.2.3阳极氧化制备TiO2纳米管6
2.2.4退火处理与晶型表征....7
2.3添加剂对阳极氧化过程的影响....8
2.3.1对恒压阳极氧化的影响8
2.3.2对恒流阳极氧化的影响....10
2.4本章小结..12
3添加剂对TiO2纳米管形貌的影响.13
3.1高分子添加剂对TiO2纳米管形貌的影响...13
3.1.1常规电解液中制得的TiO2纳米管的形貌....13
3.1.2PEG及其浓度对TiO2纳米管形貌的影响....14
3.1.3PVA及其浓度对纳米管的形貌的影响...16
3.2MBP与LA对TiO2纳米管形貌的影响17
3.3恒流氧化电流密度对TiO2纳米管形貌的影响.18