简单盐溶液的镀锌三价铬蓝白钝化工艺研究
关键字： 镀锌；三价铬；蓝白钝化Study on Trivalent Chromium Blue White Passivation Technology by Simple Salt Solution for Zinc Coating
Abstract: This paper describes a simple salt solution galvanized blue trivalent chromium passivation process research. Using single factor method to study the chromium trichloride material as the main film passivation solution optimum content of each component. And likewise studied by single factor passivation solution pH, temperature and time on the passivation film passivation effect. Get the recipe is simple, inexpensive, easy to prepare, can basically meet the requirements of ordinary workpiece antiseptic blue passivation solution. The process as follows: Chromium chloride 25 ~ 30g / L, ammonium fluoride, 1g / L, sodium 8g / L, cobalt nitrate 6g / L, pH value of 2.1, at 20℃ by the passivation 15 seconds. With 5% lead acetate solution drip time determination illustrates the process under the best conditions for corrosion resistance of the ordinary decorative chromium corrosion requirements. Obtain passivation film appearance was uniform, fine, no hair spray, blue pure. This solution is of low toxicity, low prices. Can be used for a decorative less demanding requirements based antiseptic properties of blue passivated galvanized surfaces, to the appropriate cost savings.
Key Words:Zinc coating；Trivalent chromium；Blue passivation
目 录
1引言 1
1.1 课题概况及研究的意义 1
1.1.1 课题概况 1
1.1.2 研究的意义 2
1.2 课题研究的内容及目的 2
1.3 课题在国内外研究的情况及发展趋势 2
1.3.1 课题在国内外研究的情况 2
1.3.2 课题在国内外研究的发展趋势 4
1.4 课题主要的技术要求 5
1.4.1 镀锌层主要技术要求 5
1.4.2 钝化主要技术要求 5
2三价铬钝化原理 6
2.1 钝化成膜机理 6
2.2 钝化液中各组分的作用 7
3工艺研究方法 8
3.1 工艺研究方法 8
3.2 钝化膜性能测定、试验方法 8
3.2.1 外观质量检测 8
3.2.2 耐蚀性检测 9
4实验研究 10
4.1 实验仪器、材料和试剂 10
4.2 镀锌层的制备 11
4.2.1 镀锌配方及工艺参数 11
4.2.2 镀液的配制 11
4.2.3 活化和出光 11
4.2.4 钝化用试片的电镀 11
4.3 钝化膜的制备 12
4.3.1 钝化液的配制 12
4.3.2 钝化膜的制备 12
4.4 钝化工艺的确定 12
4.4.1 三氯化铬的确定 12