涂料型钙钛矿锰氧化物涂层热辐射特性研究
用傅里叶红外光谱仪测量涂层样品在常温下反射率，根据反射计光学法间接测量涂层在常温下的发射率。分析同种材料随着涂料液体中粉末百分比含量的变化，其发射率变化的规律。实验结果表面样品涂层发射率在常温下随着粉末含量的增加而减小。分析涂层样品的反射率光谱，发现基料会对涂层的反射率光谱有一定的干扰作用。
关键词 热致变色 涂层 反射率 发射率
Title Investigation on thermal radiation properties of the perovskite-type manganese oxides coating
Abstract
With the development of aerospace industry, smart radiation surface based
on variable emissivity materials is favored by researchers because it is
more attractive than the traditional radiation surface which cannot
automatic adjust its emissivity depend on the change of environmental
temperature. Among these materials, thermochromic material has been
investigated in recent years. Therefore, this material has a good
application prospect in spacecraft thermal control and it is significant
to investigate its thermal radiation properties. This article mainly
explores the methods for preparing the perovskite-type manganese oxides
coating and studies its thermal radiation characteristics.
The powder of the perovskite-type manganese oxides is prepared by solid
state reaction method firstly. Manganite coating is spined on Al substrate
using the sol-gel of manganese oxide powder and acrylate resin. And then
the reflectivity of the sample at room temperature is measured by Fourier
transform infrared spectrometer. Coating emssivity is obtained according
to the reflectometer optical method. The emissivity variation influenced
by the content percentage change of the powder of the same material is
analyzed. The result shows that the emissivity of the coating increase with
the decrease of the content of the powder.
Key words Thermochromic Coating, Reflectivity, Emissivity
目 录
1 绪论 . 1
1.1 研究背景 1
1.2 国内外掺杂锰酸镧可变发射率材料的研究进展 2
1.3 目前研究所存在的问题和不足 . 4
1.4 课题的主要研究内容 . 5
2 涂料型钙钛矿锰氧化物涂层的制备 . 6
2.1 概述 . 6
2.2 热致变色材料制备方法 . 6
2.3 固相反应法制备涂料型钙钛矿锰氧化物粉末 . 8
2.4 溶胶-凝胶法制备涂料型钙钛矿锰氧化物涂层 . 11
2.5 本章小结 13
3 涂料型钙钛矿锰氧化物涂层热辐射特性研究 14
3.1 引言 14
3.2 热辐射性能的测量方法 14
3.3 涂料型钙钛矿锰氧化物涂层的热辐射特性 16
3.4 本章小节 20
4 总结与展望 22