纳米上转换环境功能材料制备研究
关键词 上转换 纳米材料 共沉淀法 溶胶—凝胶法 Title: Title: Title: Title: Study on the preparation of up-conversion environmental
functional nano-materials
Abstract Abstract Abstract Abstract: :: :
In this work,Y2-xPrxSiO5 up-conversion phosphor has been prepared by sol-gel
process and co-precipitation method, respectively X-ray diffraction
(XRD), scanning electron microscopy (SEM), infrared spectroscopy (IR),
particle size analyzer, and fluorescence spectroscopy have been employed
to characterize the properties and performances of Y2-xPrxSiO5 up-conversion
phosphor
The influence of different calcination temperature on phase change was
studied, XRD data results showed that phase change of the samples prepared
by the sol-gel method occurred in the 900-950°C, and the impact of the
different ratio of Pr3+ to Y2SiO5 on photoluminescence (PL) intensity was
also discussed, the results showed that 1% the doping amount of Pr
3+ had
the strongest fluorescence intensity; comparably, phase transition of
co-precipitation prepared samples was occurred about in the 800-900°C;
different ratio of Y to Si can affect the phase of the sample ,the results
studied on this showed that, when ratio of Y to Si was 2:1, sample prepared
by this mean was of high purity Y2SiO5
The phosphors synthesized by the two kinds of different methods were
characterized by fluorescence spectroscopy (FS), the results showed that
the phosphors prepared by sol-gel method had a better photoluminescence
(PL) intensity than that prepared by co-precipitation method
Keywords Up-conversion Nanometer Materials Co-precipitation
Sol—gel 目 次
目次 ..Ⅰ ⅠⅠ Ⅰ
1 引言..1
1.1 纳米上转换环境功能材料研究状..1
1.2 上转换材料的制备方法.4
1.3 上转换材料的应用6
1.4 本课题的研究目的7
1.5 本课题研究内容.8
2 溶胶—凝胶法制备样品及表征.9
2.1 试剂与仪器9
2.2 溶胶—凝胶法制备样品 Y2SiO5：Pr
3+
.9
2.3 样品 Y2SiO5：Pr
3+
的表征.9
2.4本章小结.14
3 共沉淀法制备样品及表征16
3.1 共沉淀法制备样品 Y2SiO5：Pr
3+
..16
3.2 样品 Y2SiO5：Pr
3+
的表征.16
3.3 本章小结.22
4 两种方法的比较.23
4.1 两种方法制得上转换荧光粉颗粒的粒径比较.23
4.2 两种方法中煅烧温度对晶型的影响比较23
4.3 两种方法制得上转换荧光粉荧光发光的比较23
结 论..25