铝灰法制备PAC的新工艺初探
关键词 铝灰法 PAC制备 工艺 稳定性 原料 产物 表征
毕业论文设计说明书外文摘要
Title The New Preparing Technology of Polyaluminium Chloride from Aluminum Ash
Abstract
This paper studies the stability of a new process for preparation of PAC using aluminum ash. The PAC was obtained by using acid method, which used the neutral aluminum mortar as raw materials prepared by our research group. The composition of the raw materials, the neutral aluminum mortar, products and waste residue were analyzed by VIS-723 spectrophotometer, AA240FS-GTA120 atomic absorption spectrophotometer, AFS-830 atomic fluorescence spectrometer, VISTA-MPX inductively coupled plasma emission spectroscopy. Their particle size and appearance were characterized by laser particle size measurement system and SEM. The stability of the new process for preparation of PAC was verified by using 3 kinds of aluminum ash with different sources. The results showed that the metal ions were detected in the product and they were under the limitation of the national standard, except Pb. The dimension of the samples were within the range of 6.29~9.99μm. They were verified by the experiments that the alumina average amount and basicity of the product PAC were 10.40%, 10.27% and 10.30%, 50.07, 44.98 and 30.20, respectively. Those indicated that the process had made a well fundamental for the setup of the new process for preparation of PAC using aluminum ash.
Keywords aluminum ash, PAC preparation, process, raw material, product, characterization
目 录
1 引言 1
1.1 PAC的工业合成方法 1
1.1.1 活性氢氧化铝法 1
1.1.2 三氧化二铝法 1
1.1.3 结晶氯化铝法 2
1.1.4 铝灰法 2
1.1.5 铝灰制备PAC 2
1.2 存在问题 3
1.3 课题提出研究内容及研究意义 3
1.3.1 课题的提出 3
1.3.2 研究内容及意义 3
2 实验原理 5
3 实验方案设计 5
4 实验部分 7
4.1 实验仪器和药品 7
4.2 实验步骤 7
下一篇：常规阻垢剂低温环境下作用效果研究