纳米紫外屏蔽剂的制备及性能研究
毕业论文关键词：模板法 纳米球型氧化锌 紫外屏蔽性能
Preparation and Properties of Nano UV Shielding Agent
Abstract: This paper mainly adopts a certain proportion of styrene, ammonium persulfate, acrylic acid, polyvinyl pyrrolidone (PVP) fully stirring and nitrogen into the and oil bath heating to a certain temperature, later joining initiator potassium persulfate, isothermal reaction 10 hours, after centrifugation washing system for preparation of anionic PS template. Take 0.1ps template (solid content is 1%) by adding a certain amount of water, with magnetic stirring heating to 60 ℃, constant temperature reaction 1 hour, with injection machine into a certain amount of Zn(NO3)2•6H2O, isothermal reaction 3 hours, with injection molding machine into a certain amount of ammonia, reaction for 2 hours, centrifugal washing and finally into the muffle furnace up to calcined at a certain temperature for 3 hours. The results showed that the nano zinc oxide hollow spheres of the optimum preparation process for, PS template particle size in 393-399nm, Zn(NO3)2•6H2O dosage for 0.2975g and ammonia of the injection volume 200ul, calcination temperature to 500 ℃, then prepared zinc oxide hollow spheres UV shielding performance is the best.
Keywords: Template Nano-type zinc oxide UV Shielding Agent
目录
1 绪论 1
1.1 纳米材料.. 1
1.1.1 纳米材料的发展 ..1
1.1.2 纳米材料的制备.2
1.1.3 纳米材料的光学性质 2
1.2 紫外屏蔽剂..3
上一篇：柠檬油微乳体系的制备与研究
下一篇：薄荷香型卷烟的加料加香研究