Title Nano fiber adsorbed uranium in aqueous phase
Abstract
Nanofibers membrane was prepared by electrospinning a spinning solution of polyacrylonitrile spinning, and then be amidoxime of optimization. Scanning electron microscopy (SEM) was used to characterize the functional structure, surface morphology and fiber size of nanofibers membrane. Using fourier transform infrared spectra (FT-IR) to compare and judge the most suitable temperature, pH, reaction time and concentration of amidoxime. The adsorption performance of nanofiber membrane was determined by adsorption experiment of uranyl ion. The results showed that the adsorption of nanofiber membrane was 24.2 mg/g after the fiber placed in the uranyl nitrate solution three hours.
Keywords electrospinning amidoximation optimization adsorption
目 次
1 引言 1
1.1 能源的使用现状 1
1.2 海洋核资源的开发 1
1.3 放射性物质的处理 2
1.4 纳米纤文 2
1.4.1 纳米纤文的发展 3
1.4.2 静电纺丝的发展 3
1.4.3 静电纺丝技术原理 4
1.5 静电纺丝的应用 5
1.5.1 生物制品 5
1.5.2 过滤材料 5
1.6 研究工作方向的确定 5
2 实验部分 7
2.1 实验材料及试剂 7
2.2 实验仪器 7
2.3 实验流程图 8
2.4 纺丝溶液的制备 8
2.5 静电纺丝纳米纤文膜的制备 8
2.6 静电纺丝纳米纤文膜的偕胺肟化 9
2.6.1 pH的条件优化 9
2.6.2 温度的条件优化 9
2.6.3 浓度的条件优化 10
2.6.4 反应时间的条件优化 10
2.7 静电纺丝纳米纤文膜对铀酰离子的吸附实验 10
2.8 实验小结 10
3 结果与讨论 11
3.1 聚丙烯腈组分分析 11
3.1.1 FT-IR光谱分析 11
3.2 操作环境对静电纺丝性能影响因素 11
3.3 聚丙烯腈偕胺肟化的条件优化结果分析 12
3.3.1 溶液的pH对偕胺肟化的影响 12
3.3.2 溶液的浓度对偕胺肟化的影响 13
3.3.3 溶液的温度对偕胺肟化的影响 14
3.3.4 反应时间对偕胺肟化的影响 14
3.4 聚丙烯腈纳米纺丝纤文对铀酰离子吸附性能研究 15
3.5 分析小结 16
结 论 17