Cu2O/TiO2纳米材料合成研究
毕业论文关键词：Cu2O/TiO2；水热法；浸渍还原法；乙酰甲胺磷。
Research on the Synthesis of Cu2O / TiO2 Nanomaterial
Abstract: The hydrothermal synthesis was used to prepare the nanotubes material.The Cu2O/TiO2 nanocomposites have been obtained by impregnation reduction method. The Cu2O/TiO2 nanocomposites was characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM) for analysising.We explored the degradation effect of nano-TiO2 and composite material on acephate. The results showed that when Cu2O is adhered to the surface of the synthetic material, the degradation rates of TiO2 photocatalytic on pesticides can be up to 80% within 210 min.
Key words: Cu2O/TiO2; Hydrothermal method; Impregnation reduction method; Acephate.
目 录
摘 要 1
引 言 1
1 实验部分 2
1.1 实验仪器和试剂 2
1.2 Cu2O/TiO2纳米材料的合成 2
1.3 样品的表征 3
1.4 光催化性能的评价 3
2 .结果与讨论 3
2.1 红外分析 4
2.2 XRD分析 5
2.3 SEM分析 5
2.4 光催化降解分析 6
结 论 7
参考文献 8
致 谢 10
Cu2O/TiO2纳米材料合成研究
引 言
水热法最典型的特点是前期只需一次高温高压，后期不需要进行晶化处理，不但制备过程无污染，而且制得的粉体颗粒均匀，团聚程度相对较低，产物纯净故而倍受应用[1-2]。本文采用水热法使用钛白粉制备纳米材料。
先前有众多的科研工作者把目光投向TiO2粉末，关于TiO2粉末的研究成果屡见不鲜，随着时代的进步，TiO2粉末因难以回收利用违背了可持续发展的需要而使其实际应用受到了很大的限制。半导体纳米TiO2的化学性质稳定，无毒，能够有效去除掉污染物，已经成为环保理想材料，频频有人在这方面做文章[3]。然而TiO2狭窄的可吸收波长范围，会导致太阳能资源浪费[4]。另外，TiO2在吸收紫外光后先产生光生电子空穴对而后立即恢复原状[5]，而光生电子空穴对的数量多少直接影响光催化效率的大小。科研工作者于是对TiO2的结构进行改善希望提高它的光催化活性让其更好的为人类服务。可见光催化材料中Cu2O是很好的一种，相比较于其他的半导体，它能被可见光刺激而引发的较大波长范围[6]自然而然就占据了优势。Cu2O光催化性能强并且来源广泛，无毒，价格便宜，但是作为光催化剂时生成的载流子数量容易减少，一旦减少直接就降低了它的有效率。当人为地使Cu2O与TiO2复合在一起时，可见光受激引发的电子很可能发生位置的改变，使空穴中心数量增加，数量的增加进而提高了它的效率 [7-8]。
本论文采用水热法制备纳米材料，采用浸渍还原法[9-10]进行Cu2O/TiO2纳米材料的合成。
1.实验部分
1.1 实验仪器和试剂
电子分析天平（梅特勒-托利多（上海）有限公司），81-2型恒温磁力搅拌器（上海司乐仪器厂），玻璃仪器气流烘干器（KQ-8,巩义市予华仪器有限责任公司），KQ2200型超声波清洗仪（上海易净超声波仪器有限公司）。