摘要：二氧化钛纳米管由于具有特殊的管状结构，比表面积高，电子传输速度快，在催化、光电、药物传输和吸附等领域有广阔的应用前景。因此，制备钛酸盐纳米管对开展上述研究有重要的意义。本论文以氢氧化钠和P25二氧化钛粒子为主要原料，通过在120摄氏度的不锈钢反应釜中进行水热反应，制备并得到钛酸盐纳米管。接着，对产生的钛酸盐纳米管进行不同温度的煅烧，获得了不同晶形和结构的二氧化钛纳米管，进而对所得产物进行结构和形貌的表征。研究结果显示，已制备得到了二氧化钛纳米管，且随着煅烧温度的提高，产物的晶形有明显变好的趋势。81447

毕业论文关键词：钛酸盐纳米管，制备，结构，形貌

Preparation of titanate nanotube

Abstract: Because of its special tubular structure, high specific surface area and high electron transport speed, TiO2 nanotubes have broad application prospects in catalysis, optoelectronics, drug transport and adsorption。 Therefore, the preparation of titanate nanotubes is important for the above research。 In this paper, sodium titanate and P25 titania particles were used as the main raw materials, and the titanate nanotubes were prepared by hydrothermal reaction in a stainless steel reactor at 120 degrees centigrade。 Then, the titanate nanotubes were calcined at different temperatures, and the titania nanotubes with different crystal shapes and structures were obtained。 The structures and morphologies of the products were characterized。 The results show that titania nanotubes have been prepared, and the crystal shape of the products is obviously improved with the increase of calcination temperature。

Keywords: titanate nanotubes, preparation, structure, morphology

目 录

中文摘要

ABSTRACT

1  前 言 1

 1。1钛酸盐纳米管的研究背景。 1

 1。2钛酸盐纳米管的研究现状 2

  1。2。1钛酸盐纳米管的国内研究现状 2

  1。2。2钛酸盐纳米管在国外研究现状 3

 1。3二氧化钛纳米管的优缺点 3

 1。4钛酸盐纳米管的制备方法 4

  1。4。1水热法 4

  1。4。2模板法 4

  1。4。3阳极氧化法 4

 1。5钛酸盐纳米管的应用 5

  1。5。1在石油化工方面的应用 5

  1。5。2在环境保护方面的应用 5

  1。5。3在太阳能电池方面的应用 6

  （1）基于Ti片的背光式的染料敏化太阳能电池 6

  （2）基于FTO的直射式染料敏化太阳能电池 7

  （3）基于TiO2纳米管的量子点的太阳能电池 7

  （4）本体异质结太阳能电池 7

  1。5。4在医学方面的应用 8

2  实验部分 9

 2。1主要研究内容 。9

 2。2实验原料 9

 2。3实验仪器的介绍 9

  2。3。1不锈钢高压反应釜