摘要TiO2是一种运用十分广泛的半导体材料，它的光催化降解能力在环境问题日益严重的现在具有很高的研究价值。为了研究TiO2的光催化性能，本课题采用胶溶法制备TiO2溶胶，并加入不同含量的AgNO3，以及2％的N，制成四个溶胶样品。采用浸渍提拉法制备薄膜并与溶胶一起放入干燥箱60℃干燥一段时间，制备薄膜和粉末样品。用紫外分光光度计测量几个溶胶和薄膜样品降解亚甲基蓝的吸收光谱，又表征了薄膜和粉末的XRD曲线，用DSC热分析仪表征了热失重与反应，AFM原子力显微镜分析了表面形貌，从四个样品的降解率曲线看来，Ag含量为0。2%的样品降解亚甲基蓝的能力最好。87682

毕业论文关键词  二氧化钛  光催化  银掺杂   降解

毕业设计说明书外文摘要

Title    Photocatalytic properties of Ag doped nano TiO2 sol 

Abstract TiO2 is a kind of widely-used semiconductor materials。 Its photocatalytic property has high research value for environment problems now。 To study the degradation property of TiO2, this project adopts glue method to prepare TiO2 sol solution, and adding different amounts of AgNO3, and 2% N to make four aerosol samples。 Thin film prepared by dip coating method and sol are together putted into the drying box in 60 degrees centigrade for several time to prepare thin film and powder samples。 Absorption spectra of degradation of methylene blue of several sol and film samples are measured by UV points spectrophotometric meter, and the samples are characterized by XRD curve, DSC thermal analyzer and atomic force microscopy (AFM)。 From the result, the degradation of methylene blue ability of 0。2% Ag content sample is the best。

Keywords  titanium dioxide  photocatalytic  Ag doped   degradation

1  引言 1

1。1  TiO2的概述 1

1。1。1  TiO2光催化反应的机理 1

1。1。2  TiO2的优点及缺陷 2

1。1。3 提高TiO2光催化性能的方法 2

1。1。4  TiO2光催化技术的应用 3

1。2  掺杂Ag的TiO2的制备方法 3

1。2。1 溶胶凝胶法 3

1。2。2 光化学沉积法 4

1。2。3 阳极氧化法 4

1。2。4 水热法 4

1。2。5 胶溶法 4

1。3 课题的目的和主要内容 5

1。3。1 课题的目的 5

1。3。2 课题的主要内容 5

2  实验方法 5

2。1 胶溶法制备TiO2溶胶 5

2。2 浸渍—提拉法制备TiO2薄膜 7

2。3 主要检测设备 7

2。3。1 紫外可见分光光度计 7

2。3。2 X射线衍射仪 7

2。3。3 DSC热分析仪 7

2。3。4 AFM原子力显微镜 8

2。3。5 接触角测量仪